Mechanical alloying was performed using planetary high energy ball mill with 400 rom and ball to powder ratio 15:1 for 24 hours. Bulk Ni-TiC composites (with TiC content varying from 5 to 50 wt%) were fabricated via mechanical alloying followed by SPS at 50 MPa pressure and 900-1200 C temperature. There is an increase in microhardness as